Tipo da ReferênciaJournal Article
Sitemtc-m21b.sid.inpe.br
Código do Detentorisadg {BR SPINPE} ibi 8JMKD3MGPCW/3DT298S
Identificador8JMKD3MGP5W34M/3HE6FL9
Repositóriosid.inpe.br/mtc-m21b/2014/11.19.00.01.28   (acesso restrito)
Última Atualização2015:02.10.14.22.09 administrator
Metadadossid.inpe.br/mtc-m21b/2014/11.19.00.01.29
Última Atualização dos Metadados2018:06.04.03.04.34 administrator
DOI10.1016/j.apsusc.2014.05.047
ISSN0169-4332
Rótuloscopus 2014-11 OliveiraOlivReisCarr:2014:EfNiHi
Chave de CitaçãoOliveiraOlivReisCarr:2014:EfNiHi
TítuloEffect of nitrogen high temperature plasma based ion implantation on the creep behavior of Ti-6Al-4V alloy
Ano2014
Data de Acesso28 nov. 2020
Número de Arquivos1
Tamanho2011 KiB
Área de contextualização
Autor1 Oliveira, Aline Capella de
2 Oliveira, Rogerio de Moraes
3 Reis, D. A. P.
4 Carreri, Felipe de Campos
Identificador de Curriculo1
2 8JMKD3MGP5W/3C9JJ6L
Grupo1 LAP-CTE-INPE-MCTI-GOV-BR
2 LAP-CTE-INPE-MCTI-GOV-BR
3
4 LAP-CTE-INPE-MCTI-GOV-BR
Afiliação1 Instituto Nacional de Pesquisas Espaciais (INPE)
2 Instituto Nacional de Pesquisas Espaciais (INPE)
3 Universidade Federal de São Paulo (UNIFESP)
4 Instituto Nacional de Pesquisas Espaciais (INPE)
Endereço de e-Mail do Autor1 alinecapella@gmail.com
Endereço de e-Mailmarcelo.pazos@inpe.br
RevistaApplied Surface Science
Volume311
Nota SecundáriaA1_ENGENHARIAS_II A1_ENGENHARIAS_I A1_INTERDISCIPLINAR A2_ENGENHARIAS_III A2_CIÊNCIAS_AGRÁRIAS_I A2_MATERIAIS A2_SAÚDE_COLETIVA B1_GEOCIÊNCIAS B1_ODONTOLOGIA B1_QUÍMICA B1_CIÊNCIAS_BIOLÓGICAS_I B1_ENGENHARIAS_IV B1_MATEMÁTICA_/_PROBABILIDADE_E B1_MEDICINA_II B1_MEDICINA_III B1_FARMÁCIA B1_BIOTECNOLOGIA B2_ENSINO B2_ASTRONOMIA_/_FÍSICA B2_CIÊNCIAS_BIOLÓGICAS_II C_BIODIVERSIDADE
Histórico2018-06-04 03:04:34 :: administrator -> marcelo.pazos@inpe.br :: 2014
Área de conteúdo e estrutura
É a matriz ou uma cópia?é a matriz
Estágio do Documentoconcluido
Estágio do Documentonot transferred
Transferível1
Tipo do ConteudoExternal Contribution
Tipo SecundárioPRE PI
Tipo de Versãopublisher
Páginas239-244
Palavras-ChaveAluminum, Ion implantation, Nitrogen, Titanium alloys, Constant load creep tests, Creep behaviors, High-temperature plasmas, Micro-structural characterization, Plasma-based ion implantation, Simultaneous formation, Steady state creep rate, Ti-6Al-4V alloy, Creep.
ResumoNitrogen high temperature plasma based ion implantation (HTPBII) performed on Ti-6Al-4V significantly improved the creep behavior of the alloy. Treatments were performed for 1 h at a working pressure of 4 mbar and negative high voltage pulses of 7.5 kV, 30 ¼s and 500 Hz were applied on the specimens heated at 800 °C and 900 °C, respectively. Microstructural characterization of the treated samples revealed the formation of nitrided layers, with simultaneous formation of TiN and Ti2N. The most intense peaks of these compounds were obtained at higher treatment temperature, probably due to the diffusion of nitrogen into titanium. The presence of nitrides caused surface hardening up to three times higher in comparison with untreated alloy. Constant load creep tests were conducted on a standard creep machine in air atmosphere, at stress level of 319 MPa at 600 °C. Significant reductions of the steady-state creep rates (µ) were measured for martensitic Ti-6Al-4V treated by nitrogen HTPBII, reaching minimum creep rates of 0.0318 h-1 in comparison with 0.1938 h-1 for untreated sample. The improvement of the creep resistance seems to be associated with the formation of a thick nitrided layer, which acts as a barrier to oxygen diffusion into the material. In addition, the increase of the grain size generated by the heating of the substrate during the treatment can affect some creep mechanisms, leading to a significant reduction of µ. © 2014 Elsevier B.V.
AreaFISPLASMA
Tipo de Trabalhojournal article
Conteúdo da Pasta sourcenão têm arquivos
Conteúdo da Pasta agreementnão têm arquivos
Área de condições de acesso e uso
Idiomaen
e-Mail (login)marcelo.pazos@inpe.br
Grupo de Usuáriosadministrator
marcelo.pazos@inpe.br
Grupo de Leitoresadministrator
marcelo.pazos@inpe.br
Visibilidadeshown
Política de Arquivamentodenypublisher denyfinaldraft24
Permissão de Leituradeny from all and allow from 150.163
Área de fontes relacionadas
VinculaçãoTrabalho não Vinculado à Tese/Dissertação
Repositório Espelhoiconet.com.br/banon/2006/11.26.21.31
Unidades Imediatamente Superiores8JMKD3MGPCW/3ET2RFS
DivulgaçãoWEBSCI; PORTALCAPES; COMPENDEX; SCOPUS.
Acervo Hospedeirosid.inpe.br/mtc-m21b/2013/09.26.14.25.20
Área de notas
Campos Vaziosalternatejournal archivist callnumber copyholder copyright creatorhistory descriptionlevel format isbn lineage mark month nextedition notes number orcid parameterlist parentrepositories previousedition previouslowerunit progress project rightsholder secondarydate secondarykey session shorttitle sponsor subject targetfile tertiarytype url
Área de controle da descrição
atualizar 

Fechar